Boron fibers (of total mass 5kg, rho B = 2.3g/cc, σy B = 55MPa) are uniaxially introduced into 8kg of an Al matrix (rho Al = 2.7g/cc, σy Al = 10MPa). There is no porosity before and after composite fabrication.
41.6k views
2 votes
Boron fibers (of total mass 5kg, rho B = 2.3g/cc, σy B = 55MPa) are uniaxially introduced into 8kg of an Al matrix (rho Al = 2.7g/cc, σy Al = 10MPa). There is no porosity before and after composite fabrication. Calculate the density of the composite, yield strengths parallel and perpendicular to fiber orientations.

User Rinkesh Golwala
by
3.6k points

1 Answer

5 votes

Answer:

Step-by-step explanation:

Check attachment for step by step solution

Boron fibers (of total mass 5kg, rho B = 2.3g/cc, σy B = 55MPa) are uniaxially introduced-example-1
User EgyEast
by
3.8k points
Ask a Question
Welcome to QAmmunity.org, where you can ask questions and receive answers from other members of our community.

3.6m questions

4.6m answers

Other Questions

Implement this C program by defining a structure for each payment. The structure should have at least three members for the interest, principle and balance separately. And store all the payments in a structure
Solving for dominant strategies and the Nash equilibrium Suppose Andrew and Beth are playing a game in which both must simultaneously choose the action Left or Right. The payoff matrix that follows shows
The steady-state data listed below are claimed for a power cycle operating between hot and cold reservoirs at 1200 K and 400 K, respectively. For each case, evaluate the net power developed by the cycle,
Name the author the "the journey to the centre of the earth"​
The fully corrected endurance strength for a steel rotating shaft is 42 kpsi, the ultimate tensile strength is 120 kpsi, the yield strength Sy=65 kpsi, and the fatigue stress correction factor Kf = 1.96.
Link Copied!